To enhance the preservation of strawberries, a novel coating formulation was developed using chitosan (CH) and iron oxide (IO) nanoparticles (NPs) supplemented with ginger and garlic extracts and combined with varying concentrations of 1%, 2%, and 3% Fe3O4 NPs. The results of XRD revealed an average crystalline size of 48.1 nm for Fe3O4 NPs. SEM images identified Fe3O4 NPs as bright spots on the surface of the fruit, while FTIR confirmed their presence by detecting specific functional groups. Additional SEM analysis revealed clear visibility of CH coatings on the strawberries. Both uncoated and coated strawberry samples were stored at room temperature (27 °C), and quality parameters were systematically assessed, including weight loss, firmness, pH, titratable acidity (TA), total soluble solids (TSSs), ascorbic acid content, antioxidant activity, total reducing sugars (TRSs), total phenolic compounds (TPCs), and infection rates. The obtained weight loss was 21.6% and 6% for 1.5% CH and 3% IO with 1.5% CH, whereas the obtained infection percentage was 19.65% and 13.68% for 1.5% CH and 3% IO with 1.5% CH. As strawberries are citric fruit, 3% IO with 1.5% CH contains 55.81 mg/100 g ascorbic acid. The antioxidant activity for 1.5% CH coated was around 73.89%, whereas 3% IO with 1.5% CH showed 82.89%. The studies revealed that coated samples showed better results, whereas CH that incorporates Fe3O4 NP coatings appears very promising for extending the shelf life of strawberries, preserving their quality and nutritional value during storage and transportation.